YAN Mengmeng,ZHANG Wenqian,REN Jingri*.Study on the friction properties of micro patterned half-circle shape[J].Journal of Yanbian University,2016,42(03):241-245.
微凹半圆图形表面织构的摩擦特性研究
- Title:
- Study on the friction properties of micro patterned half-circle shape
- 关键词:
- 微凹半圆图形; 微凹圆图形; 密度; Stribeck曲线; 摩擦特性
- Keywords:
- Micro patterned half circle shape; micro patterned circle shape; density; Stribeck curve; friction property
- 分类号:
- TH117.1
- 文献标志码:
- A
- 摘要:
- 采用销-盘式摩擦试验机,在常温、常压及石蜡油润滑条件下,对不同密度的微凹半圆和圆图形织构进行摩擦特性试验.利用Stribeck曲线分析接触压力、图形密度、几何形状、滑动方向以及图形间距对摩擦性能的影响.结果表明,不同密度的微凹半圆图形织构,在A、B两个滑动方向下,摩擦系数的变化有明显的不同,但其变化会随着密度的增加而降低; 微凹半圆图形织构的摩擦特性好于微凹圆形织构,当摩擦为A方向、密度为15%、间距为162 μm时,微凹半圆图形织构的摩擦系数最小.
- Abstract:
- Tribological experiment on the micro patterned half-circle and circle shape of different density was carried out using pin-on-disc friction pair at normal pressure and temperature and liquid lubricating. The effects of contact force, density, geometry, sliding direction and shape spacing on tribological characteristics were analyzed by using stribeck curve. The result shows that different density of micro patterned half-circle shape on A and B sliding direction, the variation of friction coefficient was obvious differences, with the increase of the density, the variation of friction coefficient decreased. The density was 15%, the friction coefficient of A sliding direction was smallest, and the friction properties of micro patterned half-circle shape was better than micro patterned circle shape, the best spacing was 162 μm.
参考文献/References:
[1] Ronen A, Etsion I, Kligerman Y. Friction-reducing surface texturing in reciprocating automotive components[J]. Tribology Transaction, 2001,44(3):359-366.
[2] Galda L, Pawlus P, Sep J. Dimple shape and distribution effect on characteristics of stribeck curve[J]. Tribology International, 2009,42:1505-1512.
[3] Ryk G, Kligerman Y, Etsion I. Experimental investigation of laser surface texturing for reciprocating automotive components[J]. Tribology Transactions, 2002,45(4):444-449.
[4] 任靖日,赵德金,蔡荣勲.不同密度的微小凹痕减摩特性研究[J].润滑与密封,2008,33(8):23-24.
[5] Suh Min-soo, Chae Young-hun, Kim Seock-sam, et al. Effect of geometrical parameters in micro-grooved crosshatch pattern under lubricated sliding friction[J]. Tribology International, 2010,43(8):1508-1517.
[6] 王晓雷,王静秋,韩文非.边界润滑条件下表面微细织构减摩特性的研究[J].润滑与密封,2007(12):36-39.
[7] 任靖日,赵德金,蔡荣勲,等.混合及流体动力润滑下规则微小凹痕图形表面的摩擦特性研究[J].摩擦学学报,2008,28(3):198-202.
备注/Memo
收稿日期: 2016-05-17 基金项目: 国家自然科学基金资助项目(51265050)*通信作者: 任靖日(1960—),男,博士,教授,研究方向为机械摩擦学及表面工程.