金属Y和Cr共掺杂W2N薄膜的力学及摩擦学性能研究

《延边大学学报(自然科学版)》[ISSN:1004-4353/CN:22-1191/N] 卷: 第45卷 期数: 2019年01期 页码: 22-26 栏目: 基础科学研究 出版日期: 2019-02-20
Title:
Study of mechanical and tribological properties of Y and Cr co-doped tungsten nitride films
文章编号:
1004-4353(2019)01-0022-05
作者:
苏航;  顾广瑞*
( 延边大学 理学院, 吉林 延吉 133002 )
Author(s):
SU Hang;  GU Guangrui*
( College of Science, Yanbian University, Yanji 133002, China )
关键词:
W2N薄膜;  磁控溅射;  掺杂;  力学性能;  摩擦学性能
Keywords:
W2N films;  magnetron sputtering;  doping;  mechanical properties;  tribological properties
分类号:
O484.1
文献标志码:
A
摘要:
采用磁控溅射法,通过改变氩氮比率,在Si(100)衬底上成功制备了W2N薄膜,当氩氮比率为20:6时薄膜的结晶性最好.为了改善W2N薄膜的力学和摩擦学性能,采用射频和直流磁控共溅射方法分别在Si(100)和A304不锈钢衬底上制备了软质金属Y和硬质金属Cr共掺杂的W2N(Y-Cr:W2N)薄膜.在掺杂功率20～50 W范围内,当掺杂功率为30 W时,薄膜具有最大硬度,为23.71 GPa,此时样品的弹性模量为256.34 GPa; 当掺杂功率为20 W时,薄膜的平均磨擦系数最小,为0.37.这表明,金属Y和Cr的掺入使W2N薄膜的力学和摩擦学性能有了很大的改善.
Abstract:
In this paper, well-crystallized W2N films were successfully prepared by magnetron sputtering at Si(100)by changing the argon-nitrogen ratio, and the film with optimal crystallinity was obtained at the argon-nitrogen ratio of 20:6. In order to improve the mechanical and tribological properties of the W2N film, soft metal Y and hard metal Cr co -doped W2N(Y-Cr:W2N)films were prepared by RF and DC magnetron co-sputtering. In the range of doping power 20 to 50 W, at the doping power of 30 W, the maximum hardness of 23.71 GPa and the maximum elastic modulus of 256.34 GPa are obtained. The film has the minimum average tribological coefficient of 0.37 at the doping power of 20 W. With the incorporation of metal Y-Cr, the mechanical and tribological properties of the W2N film have been greatly improved.

参考文献/References:


[1] CHOU W J, SUN C H, YU G P, et al. Optimization of the deposition process of ZrN and TiN thin films on Si(100)using design of experiment method[J]. Mater Chem Phys, 2003,82(1):228-236.
[2] BAO M D, XU X B, ZHANG H J, et al. Tribological behavior at elevated temperature of multilayer TiCN/TiC/TiN hard coatings produced by chemical vapor deposition[J]. Thin Solid Films, 2011,520(2):833-836.
[3] 张楠楠,曹文慧,林丹阳,等.等离子喷涂NiCr/Cr2C3、Ni/C及其复合涂层的耐磨性能[J].沈阳工业大学学报,2019,41(1):36-41.
[4] MIKULA M, PLASIENKA D, DAVIDE G, et al. Toughness enhancement in highly NbN-alloyed Ti-Al-N hard coatings[J]. Acta Mater, 2016,121:59-67.
[5] 梁俊才,穆健刚,张凤戈,等.硬质涂层用镀膜靶材的研究[J].粉末冶金工业,2014(2):38-43.
[6] FISCHER A C. The measurement of hardness of very hard materials[J]. Surf Coat Technol, 2016,291(15):314-317.
[7] WANG M X, ZHANG J J, YANG J L, et al. Synthesis of nanoscale multilayered ZrN/W2N multilayered coatings by magnetron sputtering[J]. Surf Coat Technol, 2018,201(15):6800-6803.
[8] CHEN T, YU L H, JU H B, et al. Influence of Ag content on the microstructure, mechanical, and tribological properties of ZrN-Ag films[J]. J Nano Res, 2018,54:88-97.
[9] YUAN Z G, YANG J F, WANG X P, et al. Effect of Al content on the microstructureand mechanical properties of Mo-Al-Si-N films synthesized by DC magnetron sputtering[J]. Surf Coat Technol, 2010,204(21):3371-3375.
[10] PORNPRASERTSUK R, KOSASANG O, SOMROOP K, et al. Proton conductivity of Y-doped BaZrO3: pellets and thin films[J]. Solid State Sci, 2011,13(7):1429-1437.
[11] 郑雷磊.ZnO薄膜的制备及其特性研究[D].厦门:厦门大学,2007.
[12] ZHU H F, SUN X, KANG L M, et al. Charge transport behaviors in epitaxial BiFeO3, thick films sputtered with different Ar/O2 flow ratios[J]. Scripta Mater, 2016,115:62-65.
[13] HWANG J D, HO T H. Effects of oxygen content on the structural, optical and electrical properties of NiO films fabricated by radio-frequency magnetron sputtering[J]. Mater Sci Semicon Proc, 2017,71:396-400.
[14] MAYRHOFER P H, HOVSEPIAN P E, MITTERER C, et al. Calorimetric evidence for frictional self-adaptation of TiAlN/VN superlattice coatings[J]. Surf Coat Technol, 2004,177:341-347.
[15] ZHU M F, SO F C, NICOLET M A. Amorphous Ni-N-W film as a diffusion barrier between aluminum and silicon[J]. Thin Solid Films, 1985,245:130-135.
[16] 黄惠茹,李晓阳,张琳琳,等.淬火低碳钢硬度、残余应力和微观组织间的关系[J].学技术与工程,2017,34:191-196.
[17] REITER A E, DERFLINGER V H, HANSELMANN B, et al. Investigation of the properties of Al1-xCrxN coatings prepared by cathodic arc evaporation[J]. Surf Coat Technol, 2005,200(7):2114-2122.
[18] LI D K, CHEN J F, ZOU C W, et al. Effects of Al concentrations on the microstructure and mechanical properties of Ti-Al-N films deposited by RF-ICPIS enhanced magnetron sputtering[J]. J Alloy Compd, 2014,609:239-243.
[19] PILLOUD D, PIERSON J F, MARQUES A P, et al. Structural changes in ZrSiN films vs their silicon content[J]. Surf Coat Technol, 2004,180:352-356.

相似文献/References:

[1]金健,栾书多,顾广瑞*.CdO - ZnO复合薄膜的光电学特性研究[J].延边大学学报(自然科学版),2021,47(02):126.
　JIN Jian,LUAN Shuduo,GU Guangrui*.Optical and electrical properties of CdO - ZnO composite films[J].Journal of Yanbian University,2021,47(01):126.
[2]管雪,金健,顾广瑞.射频磁控溅射制备的CdSe薄膜的光电学性质[J].延边大学学报(自然科学版),2022,(02):138.
　GUAN Xue,JIN Jian,GU Guangrui.Optical and electrical properties of CdSe thin films prepared by RF magnetron sputtering[J].Journal of Yanbian University,2022,(01):138.
[3]戚庆碧,崔伟哲,顾广瑞.磁控溅射CdTe薄膜的光电学特性[J].延边大学学报(自然科学版),2022,(03):217.
　QI Qingbi,CUI Weizhe,GU Guangrui.Optical and electrical properties of CdTe thin - film prepared by magnetron sputtering[J].Journal of Yanbian University,2022,(01):217.
[4]崔熙林,金健,顾广瑞.磁控溅射CdSe薄膜的光学和电学性质[J].延边大学学报(自然科学版),2023,(03):212.
　CUI Xilin,JIN Jian,GU Guangrui.Optical and electrical properties ofCdSe thin films prepared by magnetron sputtering[J].Journal of Yanbian University,2023,(01):212.

备注/Memo

收稿日期: 2019-01-06
基金项目: 国家自然科学基金资助项目(51272224)
*通信作者: 顾广瑞(1970—),男,博士,教授,研究方向为功能材料物理.

更新日期/Last Update: 2019-05-20